Different approaches for creating nanocellular TPU foams by supercritical CO 2 foaming

Abstract

In this study, three different approaches were applied to obtain thermoplastic polyurethane (TPU) nanocellular foams. The TPU was synthesized with a 4, 4′-methylenebis (phenyl isocyanate) and 1, 4-butanediol (MDI/BD) hard segment system using a pre-polymer method. The three approaches included increasing the hard segment content, adding a graphene nucleation agent, and replacing the soft segments. Although the synthesized TPUs had a different hardness, it was possible to obtain nanocellular structures with all of the methods. The cell structure is not a function of hardness only. Crystallinity affects the cell structure as well. The addition of graphene and replacement of the soft segments were more effective at yielding nanocellular foams. Our best results showed that after adding 0.1 wt% of graphene, the average cell size of the TPU foam decreased to 715 nm, and the cell density was improved to 4.94 × 10¹¹ cells/cm³. The relative density of the foam could be as low as 0.77. This study first reported elastomer-based nanocellular structures with such low relative density.

http://ift.tt/2lhvqTp